Material Property
Normal/ Bestin Matt finish/ Non Scrath Deco Sheet
Performance
Normal
Bestin
Non - Scracth
Test Method
Gloss (60 Gloss meter)
7(+-)3
2(+-)1
20(+-)5
ASTM D 2457
Tensile Strength (kgf/cm2)
350 min
350 min
350 min
JIS-K-6734
Tear Strenght (kgf/cm2)
90 min
90 min
90 min
JIS-K-6734
Heated Elongation (90C x 3min)
300% min
280% min
280% min
ASTM D 638
Charpy Impact Strength (kgfcm/cm2)
6 min
6 min
6 min
JIS-K-7111
Heat Softening Temperature (C)
70 min
70 min
70 min
JIS-K-6734
Heat Shrinkage (80C x 30min)
3% max
3% max
3% max
JIS-K-6734
Scrath resistance at 500g load pencile test
F min
H min
H min
JIS-K-5400
Chemical resistance (EA, Acetone, Etc)
o-0
o
JIS-K-7102
Material Property
High Gloss Deco Sheet
Performance
Specification
Test Method
Gloss (60 Gloss meter)
91 (+-)1
ASTM D 2457
Tensile Strength (kgf/cm2)
350 min
JIS-K-6734
Tear Strenght (kgf/cm2)
120 min
JIS-K-6734
Heated Elongation (120C x 2min)
Stress at break (g)
200 min
800 min
ASTM D 638
Charpy Impact Strength (kgfcm/cm2)
50 min
JIS-K-7111
Heat Softening Temperature (C)
77 (+-)2
JIS-K-6734
Heat Shrinkage (80C x 30min)
3 max
JIS-K-6734
Taber abrasion resistance (mg) CS-10, 1KG, 100 cycle
50 max (6.6 x 10.5)
  
Scrath resistance at 500g load pencile test
F min
JIS-K-5400
W-O-Meter (Xenon arc) 400hr
No appreciable change
JIS-K-6734
Chemical resistance (EA, Acetone, Etc)
No appreciable change
JIS-K-7102